Membrane-vacuum adhesive Robust A-154.3v

Glue for the production of cabinet furniture
Polyurethane adhesive dispersion for membrane-vacuum pressing. Suitable for molding PVC, PP, etc. films under the action of molding presses (with and without membrane) on wood-based relief parts. It is recommended to use with a hardener to increase heat resistance.

The scope of membrane-vacuum pressing is very wide: these are voluminous furniture facades made of MDF, and door leaves, and rounded tabletops, and various decorative elements of furniture. The lining of all these objects is carried out using a vacuum press (with or without a membrane). As a rule, PVC films with a thickness of 0.3-0.5 mm (rarely 0.25 mm) are used in production, plain, with a printed pattern, texture.

Advantages:

Perfectly sprayed;
Good activation;
Low reactivation temperature, 55-65°C, which allows gluing even with thin films
Characteristics:
Base: Polyurethane dispersion
White color
Thinning/Cleaning: With water
Density: 1.05 g/cm3
Viscosity: 1800±300 mPa s (Shsp. No. 4, 20 rpm)
Application Method: Spray
Time after application: 48 hours

Drying time: about 30 min at normal temperature
Glue application: from 80 to 150 g/m2 depending on the material
Activation temperature 55-65°C
Curing time: 5-7 days
Temperature resistance of the glue line Without hardener 70°C with 5% hardener 100 – 120°C *(depending on the type of film and pressing) *(depending on the type of film and pressing)
Shelf life: 6 months